ASTM G65-Procedure A weight loss 0.18 g max.DUROXITE astm g65 chromium carbide overlay plates101 HARDOX astm g65 chromium carbide overlay platesBASE PLATE A chromium-rich overlay deposited on Hardox astm g65 chromium carbide overlay plates450 base plate.Bulk hardness Single pass 55 to 57 HRC,double pass 56 to 59 HRC,triple pass 58 to 63 HRC Carbide hardness 1700 HK Volume fraction of primary carbides 30-50% ASTM G65-Procedure A weight loss 0.18
ASTM G65-Procedure A weight loss 0.18 g max.Bulk hardness Double or multiple passes 59-62 HRC alternative to tungsten carbide overlay.The specially formulated materials in Duroxite 300 result in a product with chromium overlay plate as measured in a continuous high impact lab test.In addition,the overlay thickness for Duroxite Related searches for astm g65 chromium carbide overlay plastm g65 pdfastm g65 testingSome results are removed in response to a notice of local law requirement.For more information,please see here.Previous123456NextRelated searches for astm g65 chromium carbide overlay plastm g65 pdfastm g65 testingSome results are removed in response to a notice of local law requirement.For more information,please see here.12345NextDATA SHEET UP-XAnti-wear Chromium Carbide Overlay UP-X is a wear plate composed of Chromium carbides and mild steel plates.Base on our patent welding technique,UP-X has excellent performance in wear resistant. ASTM G65 Procedure A 0.140.19 (Undiluted Deposit)
Apr 10,2019 astm g65 chromium carbide overlay plates#0183;Duroxite 200 saves money and improves productivity in a wide range of applications through higher output and less maintenance..With its high proportion of extremely hard multiple alloy complex carbides deposited on a mild steel backing plate,Duroxite 200 will last much longer than common chromium carbide overlay (CCO) products.Duroxite 200 is particularly suitable forDuroxite 200 - Damatech d.o.o2) ASTM G65 is a standard test measuring sliding abrasion resistance using a dry sand/rubber wheel apparatus.ASTM G65-Procedure A is the most severe test method.3) ASTM G65 wear test is conducted at 75% depth of the overlay materials to ensure consistently good wear resistance from the top surface through to the depth of 75% of the overlayChromium Carbide Overlay Steel PlateHART-P-100 supplies a wide range of chromium carbide overlay plate,Overlay thicknesses is vary from 3mm to 30mm depending on the thickness of the base metal.Plate can also be cut to size,shaped and rolled according to customer requirements.Chromium Carbide Overlay Wear Plates [Specification] Base MaterialASTM A36(Q235B)
The wear resistance of wear plate depends mostly on the hardness,shape,size,amount and distribution of the chromium carbide hard particles.3.Bonding strength between the overlay and base plate.The overlay and base plate are very well bonding.The overlay will penetrate into base plate about 0.8mm-1.8mm,reaching up to 350Mpa in our tests.China Mining Machinery Wear Liner Wear Lining Wear Parts Certification CE,ISO 9001:2000,ISO 9001:2008 Standard AISI,GB,ASTM Surface Treatment Hardfacing Manufacturing Process Hardfacing Material Steel Alloy China Chromium Carbide Welding Wire Hardfacing Wear Chemical composition hardfacing overlay steel plate are manufactured by welding one or multiple abrasion resistant layers on Mild steel (Q235,Q345) or stainless steel (SS 304,SS 309,SS 310) base plate.The overlay alloy has a high amount of chromium carbide hard particles.
China Chromium Carbide Wear Tube Overlay Bimetallic Alloy Steel Seamless Tubes/Pipes in Coal Washery in Mining,Find details about China Carbide Wear Tube,Overlay Bimetallic Pipe from Chromium Carbide Wear Tube Overlay Bimetallic Alloy Steel Seamless Tubes/Pipes in Coal Washery in Mining 1 YRS.100.0%.Contact Supplier.1/6.ASTM G65 metal scratching abrasion test apparatus/dry sand rubber wheel wear testing machine.US $2000-$9800 / Set.1 Set (Min.Order) CN Jinan Liangong Testing Technology Co China Chromium Carbide Coating